Shell Molding

The shell-molding process employs a heated metal pattern, usually made of cast iron,

aluminum, or brass, which is placed in a shell-molding machine containing a mixture

of dry sand and thermosetting resin. The hot pattern melts the plastic, which, together with the sand, forms a shell about 5 to 10 mm thick around the pattern. The shell is then baked at from 400 to 700°F for a short time while still on the pattern. It is then stripped from the pattern and placed in storage for use in casting.

In the next step the shells are assembled by clamping, bolting, or pasting; they are placed in a backup material, such as steel shot; and the molten metal is poured into the cavity. The thin shell permits the heat to be conducted away so that solidification takes place rapidly. As solidification takes place, the plastic bond is burned and the mold collapses.

The permeability of the backup material allows the gases to escape and the casting to air-cool. All this aids in obtaining a fine-grain, stress-free casting. Shell-mold castings feature a smooth surface, a draft that is quite small, and close tolerances. In general, the rules governing sand casting also apply to shell-mold casting.

READ MORE.......

Mechanical Engineering

McGraw−Hill Primis

ISBN: 0−390−76487−6

Text:

Shigley’s Mechanical Engineering Design,

Eighth Edition

Budynas−Nisbett

for STEP BY STEP GUIDE autocad simple tutorial please visit.........

www.autocadsimpletutorial.blogspot.com

---or---

www.autocad-simple-tutorial.com