Grey cast iron.

It is an ordinary commercial iron having the following compositions :

Carbon = 3 to 3.5%; Silicon = 1 to 2.75%; Manganese = 0.40 to 1.0%; Phosphorous = 0.15 to 1% ; Sulphur = 0.02 to 0.15% ; and the remaining is iron.

The grey colour is due to the fact that the carbon is present in the form of *free graphite. It has a low tensile strength, high compressive strength and no ductility. It can be easily machined. A very good property of grey cast iron is that the free graphite in its structure acts as a lubricant. Due to this reason, it is very suitable for those parts where sliding action is desired. The grey iron castings are widely used for machine tool bodies, automotive cylinder blocks, heads, housings, fly-wheels, pipes and pipe fittings and agricultural implements.

According to Indian standard specifications (IS: 210 – 1993), the grey cast iron is designated by the alphabets ‘FG’ followed by a figure indicating the minimum tensile strength in MPa or N/mm2.

For example, ‘FG 150’ means grey cast iron with 150 MPa or N/mm2 as minimum tensile strength. The seven recommended grades of grey cast iron with their tensile strength and Brinell hardness number (B.H.N) are given in Table 2.3.

A TEXTBOOK OF Machine Design (S.I. UNITS)

[A Textbook for the Students of B.E. / B.Tech., U.P.S.C. (Engg. Services); Section ‘B’ of A.M.I.E. (I)]

R.S. KHURMI

J.K. GUPTA

2005

EURASIA PUBLISHING HOUSE (PVT.) LTD.

RAM NAGAR, NEW DELHI-110 055

Read more........